Phase equilibria studies in alumina-containing high zinc fayalite slags with CaO/SiO2 = 0.55 Part 1
Zhao, Baojun, Hayes, Peter C. and Jak, Evgueni (2011) Phase equilibria studies in alumina-containing high zinc fayalite slags with CaO/SiO2 = 0.55 Part 1. International Journal of Materials Research, 1022: 134-142. doi:10.3139/146.110464
(Some files may be inaccessible until you login with your UQ eSpace credentials)
The phase equilibria and liquidus temperatures in the ZnO-“FeO”-Al2O3-CaO-SiO2 system in equilibrium with metallic iron have been determined experimentally in the temperature range 1343 to 1553 K and for compositions relevant to a number of different non-ferrous smelting slags. The results are presented in the form of a pseudo-ternary section ZnO-“FeO”-(Al2O3 + CaO + SiO2) with CaO/SiO2 = 0.55 and (CaO + SiO2)/Al2O3 = 7.0. It was found that wustite and spinel are the major primary phases in the composition range investigated. Wustite (Fe2+, Zn)O and spinel (Fe2+, Zn)O · (A1, Fe3+)2O3 solid solutions are formed in this system, and the ZnO in slag partitions preferentially to the spinel phase.